carboxyl modified vinyl chloride-vinyl acetate-Maleic acid ternary copolymer resinTY-MC (equivalent to VMCC of DOW) |
| Features: |
This product is composed of 83% vinyl chloride, 16% vinyl acetate and 1% maleic acid, average molecular weight is about 19000, K value is about 38. |
| Solubility: |
Ketone is excellent solvent for TY-MC. |
| Application: |
This product is mainly used in refinishing paint, ship and can coating, aluminium foil varnish, gold stamping gum, shoe material adhesive, UV surfactant, UV primer, metal ink, etc.
|
| Quality standard of TY-MC hydroxyl modified ternary resin |
| Number |
Item |
Index |
test standard |
| 1 |
Appearance |
white powder |
visual inspection |
| 2 |
Whiteness |
≥80 |
GB2913-82 |
| 3 |
Component (%) |
Vinyl chloride 83±1% |
GB/T7139-2002 |
| Vinyl acetate 16±1% |
ISO |
| Maleic acid 1±0.2% |
|
| 4 |
Active functional group (carboxyl %) |
1±0.2% |
|
| 5 |
K value |
38-40 |
GB/T3401-1999 |
| 6 |
Viscosity ml/g |
44-48 |
GB/T3401-1999 |
| 7 |
Glass transition temperature ℃ |
About 72 |
GB11998-89 |
| 8 |
Average molecular weight |
About 19000 |
concluded by viscosity |
| 9 |
Particle size (60 mesh through sieve) |
100% |
GB/T6003.1 |
| 10 |
Apparent densityg/ml |
≥0.5 |
GB20022-2005 |
| 11 |
Volatile content % |
≤1% |
GB/T2914-1999 |
| 12 |
Yellow or black spot pieces/100g |
≤20 |
GB9348-88 |
| 13 |
Solubility (20%butanone toluene solution) |
colorless or yellowish, transparent |
visual inspection |
|
|
|
|
|